AISI 4340 Alloy Steel Powder

Product Information

AISI 4340 is nickel-chromium-molybdenum alloy steel with very high strength. AISI 4340 steel is a medium carbon, low alloy steel known for its toughness and strength in relatively large sections. 4340 alloy steel is generally supplied hardened and tempered in the tensile range of 930 – 1080 Mpa. Pre hardened and tempered 4340 steels can be further surface hardened by flame or induction hardening and by nitriding. The 4340 steel has good shock and impact resistance as well as wear and abrasion resistance in the hardened condition. AISI 4340 steel properties offer good ductility in the annealed condition, allowing it to be bent or formed. Fusion and resistance welding is also possible with our 4340 alloy steel. ASTM 4340 material is often utilized where other alloy steels do not have the hardenability to give the strength required. For highly stressed parts it is excellent choice. AISI 4340 alloy steel can also be machined by all customary methods. It has a favorable response to heat treatment of oil and exhibits a good combination of ductility and strength when treated thusly. Now it has been widely used in commercial and military aircraft, automotive systems, and forged hydraulic and other machine tool applications.

AISI 4340 Alloy Steel Powder Specification

Size：customized

Purity: customized

Per your request or drawing

We can customized as required

Properties（Theoretical）

ASTM 4340 Steels And Equilvalents Chemical Composition

We can customized as required

AISI 4340 Steel Grade Heat Treatment

Stress Relieving

For pre-hardened steel stress relieving is achieved by heating steel 4340 to between 500 to 550°C. Heat to 600 °C – 650 °C, hold until temperature is uniform throughout the section, soak for 1 hour per 25 mm section, and cool in still air.

Annealing

A full anneal may be done at 844°C (1550 F) followed by controlled (furnace) cooling at a rate not faster than 10°C (50 F) per hour down to 315°C (600 F). From 315°C 600 F it may be air cooled.

Tempering

AISI 4340 alloy steel should be in the heat treated or normalized and heat treated condition before tempering. The tempering temperature for depends upon the strength level desired. For strength levels in the 260 – 280 ksi range temper at 232°C (450 F). For strength in the 125 – 200 ksi range temper at 510°C (950 F). And don’t temper the 4340 steels if it is in the 220 – 260 ksi strength range as tempering can result in degradation of impact resistance for this level of strength.

Tempering should be avoided if possible within the range 250 °C – 450 °C due to temper brittleness.

Flame or Induction Hardening

As mentioned above, pre-hardened and tempered 4340 steel bars or plates can be further surface hardened by either the flame or induction hardening methods resulting in a case hardness in excess of Rc 50. AISI 4340 steel parts should be heated as quickly as possible to the austenitic temperature range (830 °C – 860 °C) and required case depth followed by an immediate oil or water quenching, depending upon hardness required, workpiece size/shape and quenching arrangements.

Following quenching to hand warm, tempering at 150°C – 200°C will reduce stresses in the case with minimal effect on its hardness.

All de-carburised surface material must first be removed to ensure best results.

Nitriding

Hardened and tempered 4340 alloy steel can also be nitrided, giving a surface hardness of up to Rc 60. Heat to 500°C – 530°C and hold for sufficient time (from 10 to 60 hours) to develop the depth of case. Nitriding should be followed by slow cooling (no quench) reducing the problem of distortion. The nitrided grade 4340 materials can therefore be machined to near final size, leaving a small grinding allowance only. The tensile strength of the 4340 steel material core is usually not affected since the nitriding temperature range is generally below the original tempering temperature employed.

Surface hardness achievable is 600 to 650HV.

Application of AISI 4340 Alloy Steel Powder

AISI 4340 steel is used in most industry sectors for applications requiring higher tensile/yield strength than 4140 steel can provide.

Some typical applications such as:

Aircraft Landing Gear

Automotive,

Oil and Gas Drilling,

Forging,

Warm and Cold Forming,

Machine Building,

Transfer Systems, like power transmission gears  and shafts.

General engineering industries and structural use  applications, such as: heavy duty shafts, gears, axles, spindles,      couplings, pins, chucks, molds etc.

Packing of AISI 4340 Alloy Steel Powder

Standard Packing:

Typical bulk packaging includes palletized plastic 5 gallon/25 kg. pails, fiber and steel drums to 1 ton super sacks in full container (FCL) or truck load (T/L) quantities. Research and sample quantities and hygroscopic, oxidizing or other air sensitive materials may be packaged under argon or vacuum. Solutions are packaged in polypropylene, plastic or glass jars up to palletized 440 gallon liquid totes Special package is available on request.

ATTs’ AISI 4340 Alloy Steel Powder is carefully handled to minimize damage during storage and transportation and to preserve the quality of our products in their original condition.