Product Code : AL-NbHfTi-Nb89%-SF
Niobium C-103 Alloy foil are composed of C-103 Niobium alloy, a complex refractory metal alloy consisting of niobium, hafnium, titanium, and additional alloying elements. C-103 Niobium alloy has excellent mechanical strength and stability and is a widely used mate. In 1965, Niobium C-103 alloy is first manufactured in America and then used in nozzle extended segment of Apollo manned lunar module rocket engine. In 1975, China succeeded in producing NbHf10Ti1Zr0.7 niobium alloy.
Please contact us if you need customized services. We will contact you with the price and availability in 24 hours.
| Product | Product Code | Purity | Size | Contact Us |
Product Information
Niobium C-103 Alloy foil are composed of C-103 Niobium alloy, a complex refractory metal alloy consisting of niobium, hafnium, titanium, and additional alloying elements. C-103 Niobium alloy has excellent mechanical strength and stability and is a widely used mate. In 1965, Niobium C-103 alloy is first manufactured in America and then used in nozzle extended segment of Apollo manned lunar module rocket engine. In 1975, China succeeded in producing NbHf10Ti1Zr0.7 niobium alloy.
Synonyms
Niobium C103, ASTM B540, Paliney 7, Nb-Hf-Ti, HfNbTi, NbHfTi
Niobium Hafnium Alloy (C103) Foil Specification
Dimensions
Size：Thickness 0.01-0.09 mm Width 30-300 mm Length >50
Standard：ASTM B393
C103
Per your request or drawing
We can customized as required
Properties（Theoretical）
Chemical Composition
| Element | Minimum weight % (Coarse) | Maximum weight % (Coarse) | Minimum weight % (Fine) | Maximum weight % (Fine) |
| Ti | 0.7% | 1.3% | 0.7% | 1.3% |
| Hf | 9% | 11% | 9% | 11% |
| Zr | <0.7% | <0.7% | ||
| W | <0.5% | <0.5% | ||
| O | <0.025% | <0.0325% | ||
| Ta | <0.5% | <0.5% | ||
| N | <0.01% | <0.01% | ||
| C | <0.015% | <0.015% | ||
| H | <0.0015% | <0.0015% | ||
| Nb | Balance | Balance |
| Compound Formula | Nb/Hf/Ti |
| Appearance | Metallic solid in various forms |
| Melting Point | 2350 ± 50°C |
| Boiling Point | N/A |
| Density | 8.85 g/cm3 |
| Solubility in H2O | N/A |
| Electrical Resistivity | 0.0000313 - 0.0000352 ω-cm |
| Coefficient of Line-expansion/10-6K-1 | 4.5 (1203˚C) |
| Recrystallization Temperature | 1038 - 1316 ˚C |
| Anneal Temperature | 871˚C |
| Elongation Brittle Transition Temperature | - 196˚C |
| Specific Heat | 0.082 BTU/°F/lb |
| Thermal Conductivity | 22.0 Btu/hr - ft2 - °F/ft (1600 °F) |
| Thermal Expansion | 3.9 in/in/°F (400 °F) |
| Monoisotopic Mass | 320.801 g/mol |
| Niobium Alloys C-103 Foil, Sheet, Strip and Plate Mechanical Property | |||
| Ultimate Tensile Strength, Min, Psi (MPa) | Yield Strength(0.2 % offset), Min,Psi (MPa) | Elongation In 1 In.(25 mm) Gage Length, Min, % | |
| Material 0.05 in. (1.3 mm) and thinner: | |||
| Room temperature | 56 000 (385) | 40 000 (275) | 20 |
| 2000 ± 25°F (1100 ± 15°C) | 21 000 (145) | 16 000 (110) | 20 |
| Material greater than 0.05 in. (1.3 mm) in thickness: | |||
| Room temperature | 54 000 (370) | 38 000 (260) | 20 |
| 2000 ± 25°F (1100 ± 15°C) | 21 000 (145) | 16 000 (110) | 20 |
C-103 High-temperature Properties
| Composition | Shape | Temperature/˚C | Tensile Strength/MPa | Temperature/˚C | Modulus of Elasticity | Break Strength/MPa |
| 10Hf, 1Ti, 0.7Zr | Sheet | 1093 | 189.8 | - | 112 490 | - |
Niobium C-103 Fabrication Process
Niobium alloy C-103 has high melting point. Fabrication process involves C-103 ingots production process and mechanical process. Niobium hafnium alloy is processed into ingots by combining electron-beam cast with vacuum consumable electrode arc furnace. Then C-103 is extruded or forged over 1200℃. After rolling and drawing under 500℃, niobium hafnium alloy C-103 is manufactured into sheets, strips, rods, wire or other fittings.
Niobium C-103 Welding
Niobium alloy C-103 has good weldability. The welding methods include argon tungsten-arc welding and electron-beam fusion welding. Welding quality depends on the purity of argon and vacuum. The purer the argon and the lower remaining pressure is, the better the welding quality will be.
Niobium C-103 Heat Treatment
Vacuum or inert gas protection is usually applied in the process of annealing, solution and aging treatment.
Applications of Niobium Alloys C-103 Foil
Niobium C-103 Alloy foil are widely used in aerospace applications because of their incredible heat resistance, as well as light-weight, competitive price, reliability, and ability to stand up to intense vibrations and cryogenic temperatures. C-103 Niobium Alloy has a melting point of 4260 ± 90ºF, and a density of 0.320 lbs. /cubic inches, making it ideal for use in space, as well as for components used within super-heated thrusters, and rocket engines. The C-103 Niobium Alloy is widely employed in the manufacturing of scramjet engine components. Niobium alloy C-103 is an excellent material for liquid rocket thruster nozzles, lightweight propulsion systems and rocket engine thrust chamber in aerospace industry. Niobium alloy C-103 is also used in the manufacture of turbopump and high-temperature jet engine parts.
Packing of Niobium Alloys C-103 Foil
Standard Packing:
Sealed bags in carton boxes. Special package is available on request.
ATTs’ Niobium Alloys C-103 foil is carefully handled to minimize damage during storage and transportation and to preserve the quality of our products in their original condition.
Chemical Identifiers
| Linear Formula | Nb-89% Hf-10% Ti-1% |
| MDL Number | N/A |
| EC No. | N/A |
| Pubchem CID | 19751102 |
| IUPAC Name | hafnium; niobium; titanium(2+) |
| SMILES | [Ti+2].[Nb+2].[Hf+4] |
| InchI Identifier | InChI=1S/Hf.Nb.Ti/q+4;2*+2 |
| InchI Key | YZMOKPJTVNUKTK-UHFFFAOYSA-N |